本书通过研究单一尺寸SiCp对镁显微组织和力学性能的影响规律，阐明颗粒尺寸对复合材料强化行为的内在影响机理。以此为依据，设计并制备(亚微米微米)双尺寸SiCpAZ91复合材料，研究(亚微米微米)双尺寸SiCp对AZ91基体显微组织和力学性能的影响规律，表征不同尺寸SiCp同AZ91基体的界面，分析双尺寸SiCpAZ91镁基复合材料的增强机理，建立双尺寸SiCpAZ91镁基复合材料的屈服强度计算公式，阐明双尺寸SiCpAZ91镁基复合材料的室温拉伸机制和断裂机理。

Chapter 1 Introduction
1.1 Research of Discontinuous Reinforced Magnesium Matrix Composite
1.2 Stimng Casting Process of Discontinuous Reinforced Magnesium Matrix Composites
1.3 Recrystallizaion Behavior of Particle Reinforced Magnesium Matrix Composites
1.4 Interface in Magnesium Matrix Composites
1.5 Fracture Mechanism of Magnesium Matrix Composites
1.6 Main Contents in This Book
References
Chapter 2 Experimental Material and Procedure
2.1 Experimental Material
2.1.1 Matrix Alloy
2.1.2 Reinforcement
2.2 Fabrication and Hot Deformation Process
2.2.1 Fabrication of SiCp／AZ91 Composites
2.2.2 Forging of the Alloy and Composites
2.2.3 Extrusion of the Alloy and Composites
2.3 Experimental Procedure
Chapter 3 Effect of Hot Deformation on the Microstructure and Mechanical Properties of SiCp／A291 Composites
3.1 Introduction
3.2 Procedure of Hot Deformation
3.3 Microstructures of As—deformed SiCp／A291 Composite
3.3.1 Microstructures of SiCp／A291 Composite Influenced by Forging Temperature
3.3.2 Microstructures of SiCp／A291 Composite Influenced by Forging Amount
3.3.3 Microstructures of SiCp／A291 Composite Influenced by Two—step Deformation
3.4 Mechanical Properties of As—deformed SiCp／A291 Composite
3.4.1 Mechanical Properties of SiCp／A291 Composite Influenced by Forging Temperature
3.4.2 Mechanical Properties of SiCp／A291 Composite Influenced by Forging Amount
3.4.3 Mechanical Properties of SiCp／A291 Composite Influenced by Two—step Deformation
3.5 Conclusions
References
Chapter 4 Micron SiCp／A291 Composites
4.1 Introduction
4.2 Microstructures of Micron SiCp／A291 Composite
4.2.1 Microstructures Influenced by the Volume Fraction of Micron SiCp
4.2.2 Microstructures Influenced by Micron SiCp Size
4.3 Mechanical Properties of Micron SiCp／A291 Composite
4.4 Room Temperature Deformation Mechanisms
4.5 Conclusions
References
Chapter 5 Submicron SiCp／A291 Composites
5.1 Introduction
5.2 Microstructures of Submicron SiCp／A291 Composites
5.2.1 Microstructures after Hot Extrusion
5.2.2 Microstructural Evolution during Hot Extrusion
5.2.3 Discussions about the DRX Mechanism of Submicron SiCp／A291 Composite
5.3 Mechanical Properties of Submicron SiCp／A291 Composites
5.4 Analysis of Room Temperature Deformation
5.5 Discussions
5.5.1 Microstructures Influenced by SiCp Size
5.5.2 Textures Influenced by SiCp Size
5.5.3 Mechanical Properties Influenced by SiCp Size
5.6 Conclusions
References
Chapter 6 （Submicron+micron） Bimodal Size SiCp／A291 Composites
6.1 Introduction
6.2 Design of Bimodal Size SiCp／A291 Composite
6.3 Microstructures of Bimodal Size SiCp／A291 Composite
6.4 Mechanical Properties of Bimodal Size SiCp／A291 Composite
6.5 Interface in Bimodal Size SiCp／A291 Composite
6.5.1 Interface between M—SiCp and Magnesium
6.5.2 Interface between S—SiCp and Magnesium
6.6 Strengthening Mechanism
6.7 Analysis of Room Temperature Deformation
6.8 Conclusions
References
Chapter 7 Conclusions